Acrylic Elastomer WA600

Typical properties:

  1. Excellent oil and heat resistance
  2. Low compression set
  3. Excellent curing properties
Physical Form Off-white to light yellow
S.G. g/cm3 1.10
Mooney Viscosity ML 1+10 @ 100℃ 38
Volatile Matter % ≤0.5%
Tg -24

Vulcanizate properties:

Compound formula PHR  
WA600 100
Process aids: Stearic acid 1.0
Process aids: Dowhon EPA 1.0
Process aids: CN-15T 0.3
Release agent: Paraffine-135 1.0
Anti ageing agent: 445 2.0
FEB black: N550 60
HAF black: N330 -
Accelerator: FD-20 1.5
Curing agent: FD-10 0.6
Rheological Properties  
Mooney scorch at 125℃ t5 min 7.0
MDR data 180℃@15min Arc 0.5  
ML, lb-in 1.225
MH, lb-in 7.932
ts2, min 1.23
T10, min 0.45
T50, min 2.51
T90, min 8.31

Physical properties Press cured:180℃ @ 10min, post cured: 180 ℃ @ 4hour
Hardness, Shore A 68
Tensile strength, Mpa 13.1
Elongation at break, % 245
Compression set, % 150℃@70h 25
Heat resistance properties 175℃@70h in air
Tb change, % -9
Eb change, % -13
Hs change, Point +2
Fluid Resistance 150℃@70h in ASTM No.1 oil
Tb change, % -7
Eb change, % +8
Hs change, Point +2
Volume Swell, % -1


It is a low to middle viscosity mooney carboxyl type acrylic elastomer, it was designed for low compression and excellent heat resistance and oil resistance product. PA500 universally used for hose and gasket.

Packing information:

WA600 is packaged in paper bag. The weight is 25kg net per bag.

Safety and handling:

  1. Store in well ventilated place.
  2. Avoid eye contact.
  3. Keep adequate ventilation during mixing or processing.
  4. Wash thoroughly any contacted skin and clothing after handling.
  5. Further safety and handing guide, can follow the products Material Safety Data Sheet.

Important Notice:

The information in this publication is based on the test performed at our manufacturer and its cooperating company facilities that we believe are reliable, your results may vary due to differences in test types and conditions.